Axalta ViterEtch ET352 Single Pack Etch Primer

New product

A single pack Polyvinyl Butyral Etch Primer (PVB) for steelwork and galvanising.

Provides good adhesion to a variety of substrates, including steel, galvanising and aluminium

Can be used as blast primer for marine plate and structural steel

Can be overcoated with a wide range ofboth single pack and two pack products Reduced wastage compared to two pack etch products

More details

£31.66

- +

Brand: Axalta

 
Product Info

A single pack PVB Etch Primer for steelwork and galvanising.

Contains zinc phosphate anti-corrosive pigment and is chromate-free

Provides anti-corrosive protection to steelwork during fabrication

Provides good adhesion to a variety of substrates, including steel, galvanising and aluminium

Can be used as blast primer for marine plate and structural steel

Can be overcoated with a wide range of both single pack and two pack products

Reduced wastage compared to two pack etch products

Preparation
Surfaces to be coated must be clean, dry and free from any material such as oil, grease, salts and dirt that might affect adhesion.
Remove loose flaking or friable material. 
Where necessary, remove weld spatter and grind smooth all rough,sharp edges and weld seams.

Galvanised steel
Thoroughly degrease with Cleaner Degreaser (Product Reference H30 or ND14) and lightly abrade any very shiny areas. 

Mild Steel 
Degrease with a Cleaner Degreaser (Product Reference H30 or ND14) and either manually abrade or blast clean to Sa2½ (ISO 8501-1:2007)
If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.

Phosphate Steel 
Degrease with Cleaner Degreaser (Product Reference H30 or ND14) and manually abrade prior to application of the Primer Coat

Stainless Steel
Degrease with Cleaner Degreaser (Product Reference H30 or ND14) and manually abrade. 

Aluminium and Alloys
Degrease with Cleaner Degreaser (Product Reference H30 or ND14) and manually abrade. 

The temperature of the ambient air, surface or paint should not fall below 5ºC during application or drying.

Application Conditions
Relative humidity should not exceed 80%. 
The surface temperature of the steel should remain at least 3ºC above the dew point.
Cold damp conditions will impair drying times and the final finish.

Recommended Finish Coats
Overcoat with Single and Two Pack Epoxy Primers

Recommended Thinners 
Do not thin

Coverage Rates
Recommended Film weight: WFT 143µm 
Theoretical coverage rate: 7.0m² per litre

Application Methods
ViterEtch CFE can be applied by the following methods.

Airless Spray: Yes
Conventional Spray: No
Brush: Yes 
Roller: No

Application Guidance 
Airless Spray
Output fluid pressure at tip 1500-2500psi, 
Tip Size 11-13 thou (0.28-0.33 mm) 

Brush / Roller 
Recommended for small areas and touch up. 

Please note: application by brush and roller will result in a reduced film thickness and is recommended only for small areas of touch up/remedial work

Drying times at a WFT at 75µm and 23ºC 
Dust Dry: 5 minutes 
Recoatable:  6-8h
Hard Dry: 15 minutes 

Cleaning Tools and Equipment
Clean equipment with 950 Thinner after use

% Volume Solids :14%
VOC content : 700-740g / litre

Safe use
This product is formulated for professional use. 
Please ensure suitable and appropriate personal protective equipment is worn during handling and application.

Contains Phosporic Acid

For more detail please consult the Product Datasheet.